Inductive heating effects on friction surfacing of stainless steel onto an aluminium substrate

Stegmeuller, M J R, Schindele, P and Grant, Richard J (2015) Inductive heating effects on friction surfacing of stainless steel onto an aluminium substrate. Journal of Materials Processing Technology, 216. pp. 430-439. ISSN 0924--136

[img]
Preview
PDF
id155_Grant_Inductive_heating_effects_on_friction_surfacing.pdf - Accepted Version

Download (4MB) | Preview
Official URL: http://www.sciencedirect.com/science/article/pii/S...

Abstract

An experimental setup was designed to compare the principal process parametric relationships with the classical approach to friction surfacing with the addition of inductive heating. The production of the flash is described quantitatively and its influence on coating geometry and mass is presented. It was found that the coating mass and thickness decreased for an increase in the rotational speed of the consumable rod; the amount of flash produced by the consumable rod also increased. However, the e_ect of an increase in this rod contact pressure on the coating thickness is insignificant, whilst the coating mass decreases with rising pressure and the coating width increases coupled with an increase in flash production. Cross sections showed good bonding quality and mechanical interlocking at the bond interface. The substrate-coating interface showed a varying degree of mechanical interlocking and the presence of cavitations. Bond strength values applying shear and push-o_ testing of up to 106 MPa and 96 MPa, respectively, could be identified.

Item Type: Article
Keywords: inductive heating, friction surfacing, parametric study, stainless steel, coating, aluminium, bond strength
Divisions: Applied Science, Computing and Engineering
Depositing User: Mr Stewart Milne
Date Deposited: 31 Mar 2015 15:39
Last Modified: 19 Dec 2017 15:05
URI: http://glyndwr.collections.crest.ac.uk/id/eprint/8285

Actions (login required)

Edit Item Edit Item